The test methodology using specimens in the shape of tubes was developed to create axial SCCs on the inner w all of the specimen, and its effectiveness was verified by performing SCC tests under LWR environment. It w as shown that the axial stress corrosion cracking was generated from the deepest point of pre-crack by modif ying the loading mode, though the crack was not created around the loading point due to compressive stress....
英字タイトル:
Stress Corrosion Cracking Test Methodology for inner axial cracks and its cracking behavior